To be used as manually applied thin-coat renders for external use, including in KABE THERM AVANT* EPS-based EWI system and KABE THERM MW EWI system based on mineral wool. Intended for use on mineral substrates (e.g., concrete,
cement render, cement-lime render) and on substrates covered with a well-bonded plastic-based paint coating. The substrate should be primed with SiSi GT before applying the product.

  • icon
  • icon
  • icon
  • icon
Base binder:silicate-organic binder;
Pigments:organic and inorganic coloured pigments, resistant to weather conditions
Colours:nnatural white and colours according to KABE and NCS colour charts or a sample provided
Textures:solid;
Grain size:1.5 mm; 2.0 mm;
Thinner:water;
Temperature of application (air and substrate):from +5°C to +25°C;
Relative air humidity:< 75%;
Vapour permeability:Sd=0,21 m (cat. V2);
Water absorption:W=0,1 kg/m2∙h0.5 (cat. W2);
Packaging:Disposable plastic packaging holding 25 kg of the product
Storage:Product should be stored in original sealed packaging, in a cool room, but protected from frost. Opened packaging should be tightly closed and used as quickly as possible.
Shelf life:18 months from the date of production printed on the packaging, with originally sealed packaging

• Resistant to adverse weather conditions
• High impact resistance
• Anti-fungal and algae protection (reduces the growth of algae and fungi)
• Wide range of colours
• Contains silicone resin

SUBSTRATE PREPARATION: Substrate should be sound/stable (without scratches and cracks), degreased, even and dry, as well as free of biological contamination and chemical effl orescence. In case of algae/fungi growth, the substrate should be cleaned mechanically and then washed with water and disinfected with ALGIZID. Old and/or dirty substrates should be washed and degreased with water and CLEANFORCE cleaning agent. Any loose layers, not bound to the substrate (e.g., loose render or fl aked coatings), should be removed. For particularly uneven substrates (from 5 mm to 15 mm), fi rst use fi lling compounds and then smooth out the wall surface with KOMBI adhesive/base coat. Minor unevenness (up to 5 mm) can be levelled out and smoothed straight away with KOMBI adhesive/base coat. An absorbent substrate should be primed with BUDOGRUNT ZG before applying levelling compounds or base coats. If the silicate-silicone render is applied on new mineral substrates (e.g., concrete, cement render, cement-lime render) – a minimum 4-week curing period is required. Before using the render in KABE THERM AVANT and/or KABE THERM MW EWI systems, all base coats of EWI systems should be applied in accordance with the requirements for external thermal insulation composite system (ETICS). Before applying the silicate-silicone render, the primed reinforcing layer has to be fully set. This can take 3-4 days in typical weather conditions.
PRIMING: The substrate should be primed with SiSi GT before applying the render. The curing period of the product applied to the substrate before applying the render is about 24 hours. To reduce the risk of the substrate colour showing through the top coat, it is recommended to use a primer with the same colour as the render.
PRODUCT PREPARATION: The packaging contains a ready-to-use product. If stored for a long time and directly before application, the product should be thoroughly mixed (with a low-speed mixer fi tted with a basket stirrer), until a smooth, homogeneous consistency is obtained. Further mixing is not recommended, as it may result in excessive aeration of the product. If required, add a small amount of drinking water (max. 0.25 l per 25 kg of the product). Quantity of added water may vary depending on the substrate type, drying conditions and application method.
APPLICATION METHOD: UUsing a stainless steel trowel, apply a thin, uniform layer of the product to the substrate. Then, use a plastic trowel to create a texture, rubbing the applied compound with circular motions.
DRYING: Typical drying time of the render applied to the substrate is approx. 6 h (at +20°C, 55% RH). Complete hardening of render after approx. 48 hours. Note: Drying time may be longer, up to several days, due to low temperatures and high relative humidity. The newly applied render should be protected against precipitation and condensation until it is fully hardened.
USEFUL HINTS: The fi nal eff ect may depend on the substrate type. Therefore, for heterogeneous substrates, it is recommended to fi rst smooth out the entire surface with KOMBI adhesive/base coat. In order to avoid colour diff erences, it is necessary to create a surface constituting a separate architectural whole in one work cycle with material from the same production batch, using the “wet on wet” method. Tools should be cleaned with water immediately after work is completed. The render should be applied and dried on dry days at air temperatures from +5°C to +25°C. Avoid applying in direct sunlight or during strong winds. In order to protect the undried render against severe weather conditions, it is recommended to use appropriate protective meshes or tarpaulins on scaff olds.